Characteristic & main applications
Excellent conformity with flange surfaces at low surface stress. For applications with low available bolt loads.
Material
Synthetic fibres and cork, bonded with NBR.
Technichal data
| Compressibility ASTM F 36 J |
% | 10 | |
| Recovery ASTM F 36 J |
min. | % | 50 |
| Stress relaxation DIN 52913 |
25 MPa, 16h / 100ºC | MPa | 15 |
| Klinger cold/hot compression 25 MPa | thickness decrease at 23ºC | % | 16 |
thickness decrease at 200ºC |
% | 22 | |
| Tightness according DIN 3535/6 |
ml/min | 0,1 | |
| Thickness increase after fluid immersion ASTM F 146 |
oil IRM 903: 5h/150ºC | % | 5 |
| fuel B: 5h/23ºC | % | 7 | |
| Density | g/cm³ | 1,0 |
Technical advice
KLINGERexpert
The many, varied demands placed on gaskets
Gasket selection with the pT diagram
Product documentation
KLINGER Hot and Cold compression test method
High temperature tightness
Surface pressures acc. DIN 28090
Gasket factors
Chemical compatibility
Technical Support
Application Overview
Important application parameters
Installation instructions
Shelf life of KLINGERSIL
Safety Information
Technical presentation
Approvals and certificates
Dimensions of the standard sheets
Sizes: 1000 x 1500 mm, 1500 x 2000mm
Thicknesses: 0,5 mm, 1,0 mm, 1,5 mm, 2,0 mm, 3,0 mm;
other thicknesses and sizes on request.
Tolerances: thickness ± 10%, lenght ± 50 mm, width ± 50mm
Function and durability
The performance and service life of KLINGER gaskets depend in large measure on proper storage and fitting, factors beyond the manufactor’s control. We can, however, vouch for the excellent quality of our products. With this in mind, please also observe our installation instructions.
 |
 |